Microtensile Bond Strength of Fiber-Reinforced and Particulate Filler Composite to Coronal and Pulp Chamber Floor Dentin

This is the authors' abstract. We don't add key points for this paper.

This ex vivo study aimed to compare the microtensile bond strength of fiber-reinforced and particulate filler composite to coronal and pulp chamber floor dentin using a self-etching adhesive system. Coronal dentin of 40 human molar teeth was exposed by cutting occlusal enamel with a low-speed saw. Teeth were then randomly divided into two groups (n = 20). The first group was left as is, while in the second group, pulp chamber floor dentin was exposed by trepanation. After placement of a self-etching adhesive system (G-aenial Bond, GC, Tokyo, Japan), groups were further divided into two sub-groups (n = 10) according to the type of composite: fiber-reinforced composite (EP, everX Posterior, GC, Tokyo, Japan) and particulate filler composite (GP, G-aenial Posterior, GC, Tokyo, Japan). Then, composite blocks were built up. Sticks (1.0 × 1.0 mm2) were obtained from each specimen by sectioning, then microtensile bond strength (μTBS) test was performed. Statistical analysis included one-way ANOVA test and Student’s t-test (p < 0.05). μTBS values were 22.91 ± 14.66 and 24.44 ± 13.72 MPa on coronal dentin, 14.00 ± 5.83 and 12.10 ± 8.89 MPa on pulp chamber floor dentin for EP and GP, respectively. Coronal dentin yielded significantly higher μTBS than pulp chamber floor dentin (p < 0.05), independently from the tested composites.