The crystal structure of monoclinic KLu(WO4)2(KLuW) crystals was determined at room temperature by using single-crystal X-ray diffraction data. The unit-cell parameters werea= 10.576 (7),b= 10.214 (7),c= 7.487 (2) Å, β = 130.68 (4)°, withZ= 4, in space groupC2/c. The unit-cell parameters of KLu1−xYbx(WO4)2were determined in relation to Yb concentration. Vickers micro-indentations were used to study the microhardness of KLuW. The linear thermal expansion tensor was determined and the principal axis with maximum thermal expansion (α₃₃' = 16.72 × 10−6 K−1), X_3', was located 13.51° from thecaxis. The room-temperature optical tensor was studied in the near-infrared (NIR) and visible range. The principal optical axis with maximum refractive index (ng= 2.113),Ng, was located 18.5° from thecaxis at 632.8 nm. Undoped and ytterbium-doped KLuW crystals were grown by the TSSG (top-seeded-solution growth) slow-cooling method. The crystals show {110}, {1̄11}, {010} and {310} faces that basically constitue the habit of the KLuW crystals.
No takes yet. Share an insight, caveat, or question.
Pujol et al. (2006) studied this question.