Block copolyesters of poly(pentamethylene p,p′‐bibenzoate) and poly(tetramethylene adipate)

Hydroxy‐terminated poly(pentamethylene p,p′‐bibenzoate) oligomers with different molecular weights were prepared. The poly(pentamethylene p,p′‐bibenzoate) oligomers showed rather high crystallinity, and some of them exhibited a monotropic smectic phase. Block copolyesters with hard segments of poly(pentamethylene p,p′‐bibenzoate) and soft segments of poly(tetramethylene adipate) were prepared by coupling the poly(pentamethylene p,p′‐bibenzoate) oligomer and a poly(tetramethylene adipate)glycol with methylene‐4,4′‐diphenylene diisocyanate in solution. The block copolyesters were characterized by IR, 1H NMR, differential scanning calorimetry, a polarized microscope, and X‐ray diffraction. The thermal transitions of the block copolyesters were dependent on the composition and the molecular weight of the poly(pentamethylene p,p′‐bibenzoate) oligomer used. The hard segments in the block copolyesters showed no liquid crystallinity and exhibited rather low crystallinity or were even amorphous. The molecular weight of the poly(pentamethylene p,p′‐bibenzoate) oligomer used influences the glass‐transition temperature and crystalline properties of the soft segments in the block copolyesters significantly. The effect on the glass‐transition temperature of the soft segments is described as the difference in miscibility between the hard and soft segments.