Effect of Midsynthesis Addition of Silica to the Synthesis Medium on the Properties of MFI-Type Zeolite Membranes

This is the authors' abstract. We don't add key points for this paper.

Thin zeolite membranes of MFI type were prepared on α-Al 2 O 3 supports by midsynthesis addition of silica in a recirculating flow system at 95 °C. The synthesis was started with the batch composition of 80SiO 2:30TPAOH:1500H 2 O which was changed to 80SiO 2:9TPAOH:1500H 2 O by addition of silica after 24, 48, or 72 h. Compared to synthesis at constant composition, it is possible to affect the rates of nucleation and crystal growth to obtain membranes with better quality by changing the overall composition of the medium during the membrane synthesis. The membranes produced with and without midsynthesis addition of silica have n -C 4 H 10 / i -C 4 H 10 ideal selectivities of 47 and 8 at 100 °C, respectively. Among these membranes, the ones formed with midsynthesis addition of silica at 24 h yielded the highest n -C 4 H 10 /CH 4 separation selectivities, which were over 20 at 25 °C. The time at which the silica is introduced to the synthesis medium is critical for the membrane quality.