Electrochemical and corrosion behaviour of stainless steels 316L and 317L in chloridised ammonium sulphate solution

The corrosion of stainless steel alloys 316L and 317L in chloridised ammonium sulphate solution at 100°C and varying pH was investigated. Alloy 316L was found to be an adequate material for use in naturally aerated solution within the pH range of 5·4–7·4. At low potentials (<0·23 V) and a high potential (0·75 V), alloy 317L shows better performance. It also exhibits better pitting resistance at high potential, however, in the potential range of 0·23–0·45 V, alloy 316L shows better corrosion resistance. The dissolution of the Mo oxide species is proposed to be the reason for the weak performance of alloy 317L in the potential range of 0·23–0·45 V.On a examiné la corrosion des aciers inoxydables 316L et 317L dans une solution chlorée de sulfate d’ammonium à 100°C et à pH variable. On a trouvé que l’alliage 316L était un matériel adéquat pour utilisation dans une solution aérée naturellement dans la gamme de pH de 5·4 à 7·4. Aux faibles potentiels (<0·23 V) et à potentiel élevé (0·75 V), l’alliage 317L montrait une meilleure performance. Il exhibait également une meilleure résistance à la corrosion par piqûres à potentiel élevé. Cependant, dans la gamme de potentiel de 0·23–0·45 V, l’alliage 316L montrait une meilleure résistance à la corrosion. On propose la dissolution d’une espèce d’oxyde de Mo comme étant la raison pour la faible performance de l’alliage 317L dans la gamme de potentiel de 0·23–0·45 V.