Diaminobisbenzothiazole chain extended polyurethanes as a novel class of thermoplastic polyurethane elastomers with improved thermal stability and electrical insulation properties

This work was devoted to the development of a new class of modified polyurethane as an electrical insulating material. For this purpose, NCO‐terminated urethane prepolymers at different NCO contents were prepared and chain extended by 6,6′‐oxybis(2‐aminobenzothiazole) (ABT) to produce thermoplastic polyurethane elastomers. All of the polymers were characterized by FTIR and 1HNMR spectroscopies and examined for their thermal, mechanical, and electrical properties. The dynamic mechanical measurements results showed two glass transitions indicating phase separation. A considerable improvement in the thermal and electrical properties in comparison to common polyurethanes was detected for these polymers. The level of enhancement in the measured properties was related to the polyol molecular weight, hard segment content, and consequently the amount of the introduced urea and benzothiazole moieties. These findings indicated the improved high service temperature performance of these materials as electrical insulator for metallic surfaces.