Mechanical Properties and Water-Vapor Permeability of Soy-Protein Films Affected by Calcium Salts and Glucono-δ-lactone

Edible films were prepared from solutions of soy protein with calcium salts and glucono-delta-lactone (GDL). Calcium salts cross-linking interactions with soy-protein isolate (SPI) could result in the formation of films with rigid three-dimensional structure. GDL contributed to the formation of a homogeneous film structure due to increased protein--solvent attraction. Tensile strength (TS) of calcium sulfate treated SPI film (8.6 MPa) was higher than the TS of calcium chloride treated SPI films (6.4 MPa) and the control SPI film (5.5 MPa). Puncture strength (PS) of calcium sulfate treated SPI film (9.8 MPa) was higher than the PS of calcium chloride treated SPI films (8.5 MPa) and the control SPI film (5.9 MPa). SPI film formulated with GDL had larger elongation at break (39.4%) than that of SPI control film (18.2%). Calcium salts and GDL-treated SPI films had lower water-vapor permeability than the SPI control film.