Electron‐beam irradiation of blends of polypropylene with recycled acrylonitrile‐butadiene rubber

One‐mm thick sheets were prepared from blends of polypropylene and recycled acrylonitrile‐butadiene rubber (rNBR) with different blend ratios. Trimethylolpropane triacrylate (TMPTA) was used as a co‐agent. Electron‐beam‐initiated cross‐linking of the sheets was carried out at a dose of 40 kGy, and 3 phr of TMPTA based on the weight of rNBR was used. Properties such as tensile strength, Young's modulus, elongation at break, swelling percentage in oil, and morphology were studied. The results showed that the tensile properties had been improved by irradiation. The studies of swelling in oil revealed a higher cross‐link density in the irradiated blends compared to that in nonirradiated blends at similar blend ratios. Scanning electron microscopy studies revealed better adhesion between the phases and rough failure surfaces with a large number of tear lines which indicated a higher energy requirement for the failure of irradiated blends compared to that for nonirradiated blends. J. VINYL ADDIT. TECHNOL., 2010.