Dynamic mechanical and thermal characterization of high-performance polybenzoxazines

Two polybenzoxazines are cured in an autoclave from the polyfunctional benzoxazine monomers, 8,8′-bis(3,4-dihydro-3-phenyl-2H-1,3-benzoxazine) and 6,6′-bis(2,3-dihydro-3-phenyl-4H-1,3-benzoxazinyl) ketone. The density and tensile properties of these polybenzoxazines are measured at room temperature. Dynamic mechanical tests are performed to determine the Tg, crosslink density, and the activation enthalpy of the glass-transition process for these two polybenzoxazines. The effect of postcure temperature on the Tg of the polymers is investigated and discussed in terms of crosslink density. Fourier transform infrared (FTIR) spectroscopy is also applied for the molecular characterization of the curing systems. Thermal properties of these polybenzoxazines are studied in terms of isothermal aging and decomposition temperature via thermogravimetric analysis. These two polybenzoxazines show mechanical and thermal properties similar to or better than bismaleimides and some polyimides. They also show very high char yield after being carbonized in a nitrogen atmosphere.