Structure and luminescence of annealed nanoparticles of ZnS:Mn

Structural and light-emitting properties of nanoparticles of ZnS:Mn annealed in vacuum at temperatures up to 525 °C are presented. Annealing the 3.5 nm particles at temperatures up to 350 °C caused growth of some particles without substantial change in the luminescence or ZnS lattice. After annealing at 400–525 °C, the high-temperature wurtzite phase of ZnS appeared, accompanied by an increase of the average particle diameter to approximately 100 nm and a rearrangement of the Mn ions. Dramatic increase in cathodoluminescence emission was also observed and is compared to the structural information obtained from electron microscopy, x-ray diffraction, x-ray absorption fine structure, and electron paramagnetic resonance measurements.