Study of magnetic domain evolution in an auxetic plane of Galfenol using Kerr microscopy

This is the authors' abstract. We don't add key points for this paper.

Galfenol (FexGa100−x), a magnetostrictive alloy (3/2λ 110–400 ppm) of Iron and Gallium exhibits an in-plane auxetic response in the ⟨110⟩ crystallographic direction. Negative Poisson's ratios have been observed in response to application of stress fields, where values of as low as −0.7 have been reported for compositions of greater than roughly 20% Ga [Zhang et al., J. Appl. Phys. 108(2), 023513 (2010)] and in response to application of magnetic fields, where values of as low as −2.5 have been reported to be expected for compositions of less than roughly 20% Ga [G. Raghunath and A. B. Flatau, IEEE Trans. Magn. (in press)]. Several models have been proposed to understand these two distinct phenomena. Galfenol samples with less than 20% Ga also exhibit an unusual response to an increasing magnetic field applied along the ⟨110⟩ direction. The longitudinal strain which increases initially with applied field experiences a dip (until ∼10 mT) before increasing again to reach saturation. The transverse strain increases and reaches a maximum value (at the same field of ∼10 mT) and then drops from the maximum by 5%–10% as magnetic saturation is approached [G. Raghunath and A. B. Flatau, IEEE Trans. Magn. (in press)].This work deals with discussing the evolution of magnetic domains in a 16 at. % Ga single crystal Galfenol sample when subjected to magnetic fields in the ⟨110⟩ direction in the (100) plane. The magnetic domains on the surface of mechanically polished Galfenol samples were imaged using Magneto-Optic Kerr Effect microscopy. Simultaneously, the strains along the longitudinal and transverse ⟨110⟩ directions were recorded using a bi-directional strain gauge rosette mounted on the unpolished bottom surface of the planar samples. The energy from the applied magnetic field is expected to grow the ⟨110⟩ oriented domains at the expense of domains oriented along all other directions. But since the plane has an easy ⟨100⟩ axis, we expect the domains to orient along the easy direction before saturating along the applied magnetic field direction. A correlation between the images recorded and the strains observed will be used to understand this shift of domains and bump in strain at low fields.