Mode I quasi–static and fatigue delamination characterisation of polymer composites for wind turbine blade applications

Ambitious electricity generation targets from renewable sources set by many governments have lead to the rapid growth of the wind energy industry over the last two decades. The need for larger wind turbine blades for increasing energy generation has considerably increased the demand and use of high performance composites in wind turbine applications, mainly in blades. A common type of failure in composite materials is delamination of adjacent layers, which can occur either due to manufacturing inconsistencies or due to in service loads. Understanding and characterising delamination is very important in order to implement damage tolerant design methodologies. The present research work focuses on the assessment of the delamination behaviour of composites for wind turbine applications. Several composite systems were tested and their fracture toughness and fatigue delamination propagation behaviour under mode I (peeling) loading conditions were evaluated. Quasi–static tests were performed and delamination initiation values were evaluated. Fatigue delamination growth rate curves (da/dN versus G Imax) were also produced. The carbon/epoxy and glass/epoxy material systems tested were compared in terms of resin type, fibre type and interfacial characteristics.