A novel method for formation of single crystalline tungsten nanotip

A point electron source is desired to improve performance of high brightness electron beam instruments. It is valuable to create nano-sized tungsten (W) tip from sharp ordinary polycrystalline W needle. The sharp W needle, which is manufactured by electrochemical etching, has been practically utilized as a cold field emission electron source. A novel method for formation of single crystalline W nanotip on the top of h-BN coated conventional polycrystalline tungsten, by supplying high voltage, has been found. The W nanotip with an apex radius as small as a few times 10 nm would be grown on the top of the polycrystalline W needle. Field emission characteristics of obtained W nanotip are measured, and the field emission microscopic (FEM) and transmission emission microscopic (TEM) images are observed. The emission current from the W nanotip is measured to exceed 0.1 mA. The FEM image shows significant electron emission from the crystallographic facets of the W single crystal. From these results, the present method for formation of the single crystalline W nanotip would be expected as a key technology to realize a point electron source with a nano-sized apex which makes it possible to improve the performance of high brightness electron beam instruments, especially tiny X-ray tubes for medical use, as well as a cantilever of scanning probe microscope.