Photoluminescence from gas-suspended SiOx nanoparticles synthesized by laser ablation

Time-resolved photoluminescence (PL) spectra are reported for gas-suspended 1–10 nm diameter SiOx particles formed by laser ablation of Si into 1–10 Torr He and Ar. Three spectral bands (1.8, 2.5 and 3.2 eV) similar to PL from oxidized porous silicon were measured, but with a pronounced vibronic structure. Particle size and composition were determined with Z-contrast transmission electron microscopy imaging and high resolution electron energy loss spectroscopy linescans of individual nanoparticles. Maximized violet (3.2 eV) PL from the gas-suspended nanoparticles was correlated with an ex situ SiO1.4 overall particle stoichiometry. Cryogenically-collected gas-suspended nanoparticles produced web-like-aggregate films exhibiting very weak PL. Standard anneals restored strong PL bands without vibronic structure, but otherwise in agreement with the PL measured from the gas-suspended nanoparticles.