High‐temperature oxidation of aniline to highly ordered polyaniline–sulfate salt with a nanofiber morphology and its use as electrode materials in symmetric supercapacitors

In this study, for the first time, aniline was oxidized by ammonium persulfate (APS) at higher temperatures without any protic acid, and APS acted as an oxidizing agent and a protonating agent. During the oxidation of aniline by APS, sulfuric acid formation occurred, and the sulfuric acid was incorporated into polyaniline (PANI) as a dopant. PANI–sulfate samples were characterized by IR spectroscopy, X‐ray diffraction, and scanning electron microscopy techniques. In this methodology, a highly ordered PANI–sulfate salt (H2SO4) with a nanofiber morphology was synthesized. Interestingly, a PANI base was also obtained with a highly ordered structure with an agglomerated netlike nanofiber morphology. PANI–H2SO4 was used as an electrode material in a symmetric supercapacitor cell. Electrochemical characterization, including cyclic voltammetry (CV), charge–discharge (CD), and impedance analysis, was carried out on the supercapacitor cells. In this study, the maximum specific capacitance obtained was found to be 273 F/g at 1 mV/s. Scan rate from cyclic voltammetry and 103 F/g at 1 mA discharge current from CD measurement. Impedance measurement was carried out at 0.6 V, and it showed a specific capacitance of 73.2 F/g. The value of the specific capacitance and energy and power densities for the PANI–H2SO4 system were calculated from CD studies at a 5‐mA discharge rate and were found to be 43 F/g, 9.3 W h/kg, and 500 W/kg, respectively, with 98–100% coulombic efficiency.