Cross-Linked Benzoxazine–Benzimidazole Copolymer Electrolyte Membranes for Fuel Cells at Elevated Temperature

Here we report new H 3 PO 4 -doped cross-linked benzoxazine–benzimidazole copolymer membranes showing high proton conductivity and long-term durability for use in proton-exchange membrane fuel cells at elevated temperatures (>100 °C). The cross-linked copolymer membranes were prepared by mixing of poly[2,2′-( m -phenylene)-5,5′-bibenzimidazole] (PBI) with 3-phenyl-3,4-dihydro-6- tert -butyl-2 H -1,3-benzoxazine ( p BUa) in N,N -dimethylacetamide, with subsequent stepwise heating to 220 °C, and even large-sized films (30 cm × 140 m) could be easily prepared. The membranes showed high proton conductivities of up to 0.12 S cm –1 at 150 °C under anhydrous conditions. Membrane–electrode assemblies (MEAs) employing the membranes showed operating voltages of 0.71 V at 0.2 A cm –2 . Furthermore, the MEAs displayed long-term durability up to 1999 cycles, with much slower performance decay, −0.03 mV h –1, than those prepared using the PBI membrane in in situ accelerated lifetime mode (load cycling testing).