Energy storage and polarization switching kinetics of (001)-oriented Pb0.97La0.02(Zr0.95Ti0.05)O3 antiferroelectric thick films

For antiferroelectric (AFE) energy storage, the stability of energy storage density and conversion efficiency against wide temperature (T) range and broad frequency (f) band is highly preferred. In this work, we investigate the energy storage and associated kinetics of polarization switching in (001)-textured AFE Pb0.97La0.02(Zr0.95Ti0.05)O3 (PLZT 2/95/5) thick films prepared by sol-gel method. A recoverable energy storage density (Wre) of ∼26.8 J/cm3 and an energy conversion efficiency (η) as high as ∼62.5% have been obtained under an electric field of 1.85 MV/cm and room temperature. Both the Wre and η are only weakly T-dependent up to 280 °C and weakly f-dependent ranging from 20 Hz to 10 kHz. The high frequency stability originates from the rapid polarization switching as identified by the nucleation-limited-switching theory, suggesting a characteristic switching time as short as ∼3 ns, favorable for applications in pulse energy storage.