Composites based on CB/CF/Ag filled EPDM/NBR rubber blends with high conductivity

For many applications of conductive rubbers, it is desirable to endow the conductive rubber with high conductivity at low conductive filler loading. In this work, composites based on ethylene‐propylene‐diene monomer (EPDM) rubber and nitrile‐butadiene rubber (NBR) were prepared using carbon blacks, carbon fibers, and silver powders as fillers. As the weight fraction of silver powder increased, the hardness of composites increased gradually while the tensile strength and elongation at break decreased. SEM revealed that the EPDM/NBR blends exhibited a relatively co‐continuous morphology. The differential scanning calorimetry (DSC) curves reported the EPDM/NBR rubber blends were incompatibility. The thermogravimetry (TG) studies showed that adding a small amount of silver powder could improve the thermal stability of composites. These conductive composites exhibited good electrical property. At room temperature, when the total volume fraction of fillers was 15.20%, the volume resistivity of EPDM/NBR blend was only 0.0058 Ω cm.