Experimental study demonstrates enhanced hardness and density in SiC-based high-entropy carbide nanocomposites, indicating strong potential for extreme-environment applications.
A dense monolithic SiC/(Hf0.25Ta0.25Zr0.25Nb0.25)C/C high-entropy ceramic nanocomposite was prepared using a polymer-derived ceramic (PDC) method combined with spark plasma sintering (SPS). The microstructural evolution and mechanical properties of the obtained nanocomposites were characterized by X-ray diffractometer (XRD), transmission electron microscope (TEM), scanning-electron microscope (SEM), and nanoindentation. The results indicate that the phase composition of SiC/(Hf0.25Ta0.25Zr0.25Nb0.25)C/C can be adjusted by modifying the metal content of the single-source precursor (SSP) through molecular design. The resulting precursor exhibits an exceptionally high ceramic yield, with mass retention of over 90% at 1100 °C, which guarantees the densification of the final SiC/(Hf0.25Ta0.25Zr0.25Nb0.25)C/C composites. The PDC route facilitates the in situ formation of a high-entropy phase within the ceramic matrix under low temperature pyrolysis conditions. Combined with SPS, a dense monolithic SiC/(Hf0.25Ta0.25Zr0.25Nb0.25)C/C nanocomposite was obtained, exhibiting an open porosity of 0.41 vol%, nano-hardness of 27.47 ± 0.46 GPa, elastic modulus of 324.00 ± 13.60 GPa, and fracture toughness of 3.59 ± 0.24 MPa·m0.5, demonstrating excellent mechanical properties.
No takes yet. Share an insight, caveat, or question.
Wang et al. (2024) studied this question.
Synapse has enriched 5 closely related papers on similar clinical questions. Consider them for comparative context: