Structure-property relations in mesoscopic BaTiO3and PbTiO3

Structure-property relations in meaoscopic BaTiO3 and PbTiO3 are reviewed from the stand-point of effects of crystallite size on intrinsic behavior using the Landau-Ginzburg-Devonshire formalism. Experimental results based on x-ray diffrdctometry and quantitative calorimetry indicate that the critical crystallite sizes (CCS) for the stabilization of the cubic paraelectric phase in BaTiO3 and PhTiO3 are in the vicinity of 67 and 15 nm, respectively. Thc CCS scales inversely with the cubic-tetragonal transition temperature (Ttr). The depression in Ttr in PbTiO3 is -15 (C with decreasing crystallite size (CS). A decrease in Ttr for BaTiO3 was not observed. Both systems preserve their first order phase transformation characteristics with reduced CS. Electrostrictive coefficients were determined as a function of CS and were found to exhibit a pronounced increase with decreasing CS. The increase in the elcctrobtrictive coefficients offsets the decrease in spontaneous polarization and results in an increase in piezoelectric moduli suggesting that strong piezoelectric activity could indeed be observed in the mesoscopic size range