Investigation of the ionisation density dependence of the glow curve characteristics of LIF:MG,TI (TLD-100)

The dependence of the shape of the glow curve of LiF:Mg,Ti (TLD-100) on ionisation density was investigated using irradiation with (90)Sr/(90)Y beta rays, 60 and 250 kVp X rays, various heavy-charged particles and 0.2 and 14 MeV neutrons. Special attention is focused on the properties of high-temperature thermoluminescence; specifically, the behaviour of the high-temperature ratio (HTR) of Peaks 7 and 8 as a function of batch and annealing protocol. The correlation of Peaks 7 and 8 with average linear-energy-transfer (LET) is also investigated. The HTR of Peak 7 is found to be independent of LET for values of LET approximately >30 keV microm(-1). The behaviour of the HTR of Peak 8 with LET is observed to be erratic, which suggests that applications using the HTR should separate the contributions of Peaks 7 and 8 using computerised glow curve deconvolution. The behaviour of the HTR following neutron irradiation is complex and not fully understood. The shape of composite Peak 5 is observed to be broader following high ionisation alpha particle irradiation, suggesting that the combined use of the HTR and the shape of Peak 5 could lead to improved ionisation density discrimination for particles of high LET.