Living polymerization of chiral aryl isocyanides, such as m- and p-menthoxycarbonylphenyl isocyanides 2 and 5, initiated by the Pd-Pt mu-ethynediyl dinuclear complex 1, proceeds with a high screw-sense selectivity to give the poly(isocyanide)s 3 and 6, which exhibit a large specific rotation and an intense CD band at lambda = 364 nm as a consequence of a helical chirality. The molar optical rotation and molar circular dichroism of the resulting polymers 3 and 6 reach a constant value at a degree of polymerization (Pn) of more than 30. Screw-sense-selective polymerization of achiral aryl isocyanides that bear very bulky substituents, such as 3,5-di(propoxycarbonyl)phenyl isocyanide (11), 3,5-di(butoxycarbonyl)phenyl isocyanide (13), and 3,5-di(cyclohexyloxycarbonyl)phenyl isocyanide (15), is achieved by the use of chiral oligomer complexes 3(30) and 6(30), prepared from the reaction of 1 with 30 equivalents of 2 or 5, as an initiator to give predominantly single-handed helical polymers. In contrast, smaller aryl isocyanides are also polymerized by 3(30) and 6(30) with screw-sense selectivity in the initial stage of the reaction, but the single-handed helix is not preserved up to high molecular weight. Kinetic studies of the polymerization of (L)- and (D)-2, or (L)- and (D)-5 with chiral oligomer complexes (L)-3(50) or (L)-6(100) suggests that the screw sense of the polymer backbone is not controlled kinetically, but rather that the thermodynamically stable screw sense is produced.
No takes yet. Share an insight, caveat, or question.
Takei et al. (2000) studied this question.