Elastic properties and mechanical relaxation behaviors of PVDF (poly (vinylidene fluoride)) at temperatures between −20 and 100 °C and at 2 MHz ultrasonic frequency

The elastic properties of PVDF have been investigated as a function of temperature. The propagation velocity and absorption of longitudinal and transverse ultrasonic waves have been measured at a constant frequency of 2 MHz and temperatures between –20 and 100 °C. Hence, the temperature dependences of storage and loss elastic constants have been obtained for temperatures between –20 and 100 °C. It has been seen that the relaxation behavior is affected from the form of mechanical disturbance. For the longitudinal mode, only one relaxation peak at 42 °C, but for transverse mode three relaxation peaks at 28 °C, 60 °C, and 94 °C have been observed. The results have been compared with the literature values obtained previously for PVDF.