Fabrication and performance of a single-crystal lead magnesium niobate-lead titanate cylindrical hydrophone

The development of a piezoelectric hydrophone based on lead magnesium niobate-lead titanate [PbMg1/3Nb2/3O3-PbTiO3 (PMN-PT)] single-crystal piezoelectric as the hydrophone substrate is reported. Although PMN-PT can possess much higher piezoelectric sensitivity than traditional lead zirconate titanate (PZT) piezoelectrics, it is highly anisotropic and therefore there is a large gain in sensitivity only when the crystal structure is oriented in a specific direction. Because of this, simply replacing the PZT substrate with a PMN-PT cylinder is not an optimal solution because the crystal orientation does not uniformly align with the circumferential axis of the hydrophone. Therefore, a composite hydrophone that maintains the optimal crystal axis around the hydrophone circumference has been developed. An 11.3 mm diameter composite hydrophone cylinder was fabricated from a single <110> cut PMN-PT rectangular plate. Solid end caps were applied to the cylinder and the sensitivity was directly compared with a solid PZT-5A cylindrical hydrophone of equal dimensions in a hydrophone test tank. The charge sensitivity showed a 9.1 dB improvement over the PZT hydrophone and the voltage sensitivity showed a 3.5 dB improvement. This was in good agreement with the expected theoretical improvements of 10.1 and 4.5 dB, respectively.