Laccase‐catalyzed synthesis of polypyrrole‐multiwalled carbon nanotube composites as energy storage materials for capacitors

Multiwalled carbon nanotubes (MWNTs) were coated with polypyrrole (PPy) using in situ enzymatic polymerization of pyrrole catalyzed by a laccase (benzenediol:oxygen oxidoreductase, EC 1.10.3.2) from Trametes versicolor. Transmission electron microscopy revealed that the MWNTs were uniformly coated with very thin layers of PPy without any indication of globular polymer aggregate formations. The enzymatic synthesis of the MWNTs/PPy composites was quite simple being performed in a one‐pot aqueous solution (pH 4.0) under mild reaction conditions. The potential of the composites with respect to the development of energy storage devices was demonstrated by fabricating a two‐electrode coin cell capacitor (diameter 20 mm, thickness 1.6 mm) utilizing the composites as electrode materials. The capacitance of the cell was 28.0 F g−1 for the electrode material as measured by a galvanostatic charge–discharge method. The energy density and power density were 2.55 and 805 W kg−1, respectively, which were close to those of the capacitors classified as ultracapacitors.