Immunohistochemical study of dental pulp applied with 4-META/MMA-TBB adhesive resin after pulpotomy

This is the authors' abstract. We don't add key points for this paper.

The purpose of this study was to investigate nerve regeneration and proliferative activity in amputated pulp tissue after the application of 4-META/MMA-TBB adhesive resin (4-META resin). Calcium hydroxide was used as a control material. At 3 days, fibroblast-like cells were positive for proliferating cell nuclear antigen (PCNA) in both 4-META resin- and calcium hydroxide-treated groups and were located mainly within 0.5 mm from the cut surface. Only a few fragmented neurofilament protein (NFP)-positive nerve fibers were observed in this area. At 7 and 14 days, the number of PCNA-positive cells had gradually decreased and regenerated NFP-positive nerve fibers were observed close to the cut surface of the pulp in both groups. At 21 days in the experimental group, several PCNA-positive cells were still found in the area 0.5 mm from the cut surface, and NFP-positive nerve fibers were detected about 0.15-;0.2 mm from the cut surface. In contrast, a dentin bridge was produced under the necrotic layer at 21 days in the control group. PCNA-positive cells were not found underneath the dentin bridge, but NFP-positive nerve fibers had regenerated close to it. These results suggest that although cell differentiation and nerve regeneration are delayed, wound healing occurred even after the application of 4-META resin to exposed pulp surface the same as calcium hydroxide application.