Eu2+luminescence in M5(PO4)3X apatites, where M is Ca2+, Sr2+and Ba2+, and X is F-, Cl-, Br-and OH$

M 5 (PO 4 ) 3 X apatites are well known for their technological importance as phosphors, laser hosts and biocompatible materials. Divalent-europium-activated alkaline earth chloroapatites are of special importance for their application as the blue component in high-efficiency trichromatic fluorescent lamps. In these apatites, Eu 2+ yields narrow-band emission in the blue region corresponding to the 4f 6 5d to 8 S 7/2 allowed electric dipole transition. It has been found that the dominant emission band observed can be assigned to Eu 2+ occupying M II sites of the apatite system having C 1h symmetry. In the case of barium chloroapatites one could also observe Eu 2+ emission from a second type of site (M I ) that is available in the apatite system. The weak emission observed in the latter can be attributed to the intense spectral overlap with the former site(s) and thermal quenching effects. The exchange coupling between the 4f 6 and 5d electrons of Eu 2+ manifests itself in 'stair-case' features in the excitation spectrum and the strength of the exchange interaction is highly dependent on the host apatite(s). Also, in the Eu 2+ , Mn 2+ co-doped system, energy transfer is found to occur from the former to the latter and the transfer is regulated by an exchange process. Various results based on these facts are discussed in detail.