Comparison of the enthalpic relaxation of poly(lactide–co‐glycolide) 50:50 nanospheres and raw polymer

The phenomenon of enthalpic relaxation was evaluated for poly(lactide‐co‐glycolide) (PLGA, 50:50), in terms of storage of nanospheres for use as a controlled drug delivery system. Samples were stored for different times and temperatures below the glass transition temperature (Tg). Relaxation occurred at a significant rate up to 15 degrees below the Tg of 39.2°C. The effect of polymer morphology was considered by comparing the relaxation kinetics of the raw polymer with that of nanospheres formed using a novel technique. The nanospheres were shown to have a larger change in heat capacity at the glass transition and a longer average relaxation time than that of the raw polymer, and the relationship between these two parameters was discussed. For both the raw polymer and the nanospheres, relaxation was found to occur at a significant rate at room temperature. The storage of this system at subambient temperatures was therefore deemed important for maintaining the physicochemical properties of the system.