Co-Pt and Fe-Pt bimetallic nanoparticles in a carbon matrix are prepared by a plasma arc process

Nanoparticle ensembles in Co-Pt and Fe-Pt systems embedded in a carbon matrix are prepared by a plasma-arc method. Two-phase samples based on disordered FCC solid solutions are prepared in both systems. In the Co-Pt system, the solid solujtions are mixed within one ensemble; in the Fe-Pt system, they are spatially separated. A magnetization hysteresis curve from Co-Pt nanoparticles (3–12 nm) fully coincides with a magnetization curve from a single-phase disordered solid solution Co 0.50 Pt 0.50 (7–9 nm) prepared at 325°C by thermolysis of the precursor double complex salt (DCS). Metal ratios, solid solution structures, and particle sizes being the same, the magnetic response is dictated exclusively by the amount of a magnetic phase of mixed and interacting particles and is independent of the distribution of the magnetic phase over the solid solution phases.