Graphene dispersions in alkanes: toward fast drying conducting inks

) was obtained when 23% of the graphene surface was covered by the polymer. In this case, the flakes were constituted of 2-5 graphene layers. More extensive exfoliation, down to single-layer graphene, was achieved at greater surface coverage, but led to inks with higher sheet resistance. Thus, by combining a tailored polymeric dispersant, a smooth exfoliation process and a low-boiling non-polar ink solvent, we were able to prepare highly-conductive fast-drying graphene inks which should have a high potentital for the development of roll-to-roll printed electronics.