Viscosity of Fayalite-Based Slags

A rotating-cylinder viscometer was used to measure the viscosity of fayalite-based melts from 1200 to 1350°C. The silica content and oxygen pressure were in the range of 22.5 to 37.5 weight per cent and 10−7 to 10-11 atmospheres. To illustrate their effects, three-dimensional viscosity surfaces were plotted at various temperatures. Viscosities generally decreased with increasing temperature, increasing oxygen pressure and decreasing silica content. However, a maximum was found near the fayalite composition. Added CaO decreased viscosity. Résumé Un viscosimètre à cylindre tournant a été utilisé pour mesurer la viscosité entre 1200 et 1350°C de mélanges fondus à base de fayalite. La quantité de silice et la pression oxygène se situaient entre 22.5-37.5 pourcentage poids et 10−7-10−11 atmosphères respectivement. Afin d'illustrer leurs influences, les surfaces tridimensionnelles de viscosité sont portées en graphique à différentes températures. Les viscosités décroissent généralement avec l'augmentation de la temperature et de la pression oxygène et avec la diminution de la quantité de silice. Toutefois, on a trouve un maximum près de la composition de la fayalite. L'addition de CaO fait diminuer la viscosité.