Multifunctional Integration of Double-Shell Hybrid Nanostructure for Alleviating Surface Degradation of LiNi0.8Co0.1Mn0.1O2 Cathode for Advanced Lithium-Ion Batteries at High Cutoff Voltage

Ni-rich LiNi 0.8 Co 0.1 Mn 0.1 O 2 (NCM811) cathode is considered to be among the most promising candidates for high-energy-density lithium-ion batteries (LIBs). However, both capacity fading and structural degradation occur during long-term cycling, which extremely limit the commercial applications of NCM811, especially at a high cutoff voltage (>4.3 V). Here, we design a double-shell hybrid nanostructure consisting of a Li 2 SiO 3 coating layer and a cation-mixed layer ( Fm 3̅ m phase) to improve its electrochemical performance. Consequently, the Si-modified NCM811 electrode shows outstanding cycling stability with a 95.2% capacity retention at 4.3 V after 100 cycles and 87.3% at a 4.5 V high cutoff voltage after 100 cycles. This designed double-shell hybrid nanostructure alleviates side reactions, structural degradation, and internal cracking, effectively enhancing the surface structural stability. This efficient strategy provides a valuable step toward further commercial applications of the LiNi 0.8 Co 0.1 Mn 0.1 O 2 cathode and enriches the fundamental understanding of layered cathode materials.