Isothermal and nonisothermal crystallization kinetics of irradiated nylon 1212

The crystallization behavior of nylon 1212, irradiated at 60Co γ‐rays (50 kGy), was studied by a rheometer, polarized optical microscopy (POM), and differential scanning calorimeter (DSC). The results showed that irradiated nylon 1212 samples exhibited abnormal crystallization behavior during the crystallization process: The Avrami exponent n was calculated and was found to be in the range from 2.06–2.41 for isothermal crystallization, and from 2.67–4.91 for nonisothermal crystallization; the spherulite morphology also changed largely by polarized optical microscopy (POM); the crystallization activation energy ΔE for isothermal and nonisothermal crystallization process of irradiated nylon 1212 are determined to be 57.4 kJ/mol and 78.65 kJ/mol, respectively, which are lower than that of nonirradiated nylon 1212. At the same time, a new method by a combination of the Avrami and Ozawa equations was successfully applied to analyze the noncrystallization process of irradiated nylon 1212.