Formation of coherent nanocomposite structure in nickel-aluminum alloys synthesized far from equilibrium

This is the authors' abstract. We don't add key points for this paper.

The present study reports on the structure formation in thin epitaxial nickel-aluminum films (Ni 1-x Al x ; Al atomic fraction x up to x = 0.24 ) grown on MgO ( 001 ) substrates by magnetron sputtering. Experimental and computational data demonstrate that for x < 0.11 , the films exhibit the face-centered cubic random solid-solution Ni 1-x Al x structure ( γ phase). Whereas in the range x=0.11-0.24 the γ phase coexists with the ordered L 1 2 structure ( γ ′ phase). The two phases are homogenously intermixed forming a strained coherent nanocomposite , which exhibits a single lattice parameter that expands as the Al content increases. Isothermal annealing of films containing x = 0.14 of Al, coupled with structural and nano-mechanical characterization, reveal that the coherent nanocomposite retains its overall integrity for temperatures up to 673 K , while the film hardness increases from 5.5 GPa (as deposited films) to 6 GPa . Further increase of the annealing temperature to 873 K and 1073 K causes the coherent nanocomposite to dissolve into distinct γ and γ ′ phase domains and the hardness to decrease down to values of 4 GPa . These findings confirm the metastable nature of the as-deposited thin Ni 1-x Al x alloy films and underpin the effectiveness of high supersaturation/undercooling for creating non-equilibrium phases and self-organized nanostructures upon synthesis of multicomponent materials.