Processing of large grain Y-123 superconductors with pre-defined porous structures

Porous superconductors have inherent cooling advantages over their bulk counterparts and, as a result, are emerging as an important class of materials for practical applications. Single-domain Y–Ba–Cu–O (YBCO) foams processed with a pre-defined, open porous structure, for example, have significant potential for use as elements in resistive superconducting fault current limiters. In this case, the interconnected porosity is ideal for producing reinforced composites with improved mechanical and heat conducting properties. In this paper we describe a few simple methods for fabricating large grain YBCO superconductors with various predefined porous structures via an infiltration process from tailored, porous Y 2 BaCuO 5 (Y-211) pre-forms manufactured by a variety of techniques, including slurry-coating of standard polyurethane foams to replicate their structure. Foams produced by this method typically have a strut thickness of a few hundred µm and pore sizes ranging from 10 to 100 pores per inch (PPI). Foams with increased strut thickness of up to millimetre dimensions can be produced by embedding organic ball spacers within the Y-211 pre-form followed by a burn-out and sintering process. Single-domain YBCO bulk materials with cellular and pre-defined 3D interconnected porosity may be produced by a similar process using tailored wax structures in Y-211 castings.