Effects of Rare‐Earth Ions on the Quality of a Li–Zn Ferrite

Effects of the rare‐earth ions on some properties of a lithium‐zinc ferrite used in high frequency are described. A set of seven compounds with formula Li0.3Zn0.4Fe1.96R0.04O4 where R  Yb, Er, Dy, Tb, Gd, Sm and Ce, were prepared by the classical method. The obtained results reveal that, by introducing a relatively small amount of R2O3 instead of Fe2O3, an important modification of both the structure and the properties can be obtained. Curie point, magnetization, electrical resistivity, density, hardness are affected by these substitutions. The effects of rare‐earth ions were explained both by their partial diffusion in the spinel lattice and by the formation of the crystalline secondary phases on the grain boundaries. Densification of the ceramic is attributable predominantly to the relative shrinkage during sintering. Le travail montre les effets des ions de terre rare sur quelques paramètres d'nne ferrite de LiZn utilisé dans la haute fréquence. Une série des sept compositions avec la formule chimique Li0.3Zn0.4Fe1.96R0.04O4 (R  Yb, Er, Dy, Tb, Gd, Sm et Ce) a été preparée par la méthode classique. Les résultants obtenus montrent que par l'introduction des petites quantités de R2O3 dans le lieu de Fe2O3 une important modification tant de la structure que des propriétés on peut obtenir. La temperature de Curie, l'aimantation, la résistance électrique et densité sont affectés. L'influence des ions de terre rare este expliqué tant par leur partiel diffusion dans la réseau spinel que par leur ségrégation à la surface des cristaux comme phases secondaires. La densification du ferrite est atribué en principal à une relative contraction pendant le frittage.