Pentacene-based low voltage organic field-effect transistors with anodized Ta2O5 gate dielectric

Pentacene-based low voltage organic field-effect transistors were realized using an anodized Ta2O5 gate dielectric. The Ta2O5 gate dielectric layer with a surface roughness of 1.3Å was obtained by anodizing an e-beam evaporated Ta film. The device exhibited values of saturation mobility, threshold voltage, and Ion∕Ioff ratio of 0.45cm2∕Vs, 0.56V, and 7.5×101, respectively. The gate leakage current was reduced by more than 70% with a hexamethyldisilazane (HMDS) treatment on the Ta2O5 layer. The HMDS treatment also resulted in enhanced mobility values and a larger pentacene grain size.