Stable Core Shell Co3Fe7–CoFe2O4 Nanoparticles Synthesized via Flame Spray Pyrolysis Approach

Air stable Co 3 Fe 7 –CoFe 2 O 4 nanoparticles have been synthesized via one-step flame spray pyrolysis of a mixture of Fe/Co precursor solution under stronger reducing atmosphere. The as-synthesized nanoparticles with diameters of 20–80 nm showed a typical core shell structure and high stability for being one month in air, whose metallic Co 3 Fe 7 cores were protected against oxidation by a surface shell of about 2–4 nm cobalt iron oxide (CoFe 2 O 4 ). The ratio of metallic Fe/Co alloy nanoparticles was 7:3. The alloy nanoparticles exhibited enhanced saturation magnetization (126.1 emu/g), compared with flame sprayed iron nanoparticles with the same conditions. The formation process of metallic alloy nanoparticles with core–shell structure was investigated, which included three stages: flame combustion, reducing, and surface oxidation during the flame process. It is reckoned that such a continuous production approach is an effective way to produce the stable Co 3 Fe 7 alloy nanoparticles with high saturation magnetization.