Diffusion studies and critical current in superconducting Nb–Ti–Ta artificial pinning center wire

The diffusion between Nb–20%Ta (wt %) and pure Ti is studied at temperatures of 973, 1023, and 1073K, for duration times among 25 and 121h in an artificial pinning center (APC) wire composed of a Ti core surrounded by a Nb–20%Ta layer. The produced diffusion layer is a ternary alloy with superconducting properties, such as critical field Bc2 and critical current density JC, which intrinsically depend on the layer composition. Measurements of layer morphology and composition were performed, and the results show a preferential diffusion of Nb and Ta into Ti. There is a slight diffusion of Ti into Nb through grain boundaries. The presence of Ta also slows down the diffusion of Nb in Ti if compared to the couple formed by pure Nb and Ti. Regarding the mechanical properties of the composite wire, the use of lower temperatures to form the ternary phase is desirable in order to avoid a larger portion of the diffusion layer rich in Ti that favorites α-Ti precipitations that are detrimental to the wire ductility. The best JC value was obtained for the sample heat treated at 973K. The improvement of the flux-line pinning was associated with a sharp change of the diffusion layer composition rather than pinning by normal layer interfaces, suggesting a new source of pinning in this kind of material. Nb–Ti–Ta ternary alloys have the potential to be used in superconducting magnets when fields above 12T are required.