Cu-doped nickel oxide interface layer with nanoscale thickness for efficient and highly stable printable carbon-based perovskite solar cell

The power conversion efficiency (PCE) of hole conductor free carbon-based perovskite solar cells (PSCs) is restricted by the poor charge extraction and recombination losses at the carbon-perovskite interface. For the first time we successfully demonstrated incorporation of thin layer of copper doped nickel oxide (Cu:NiO x ) nanoparticles in carbon-based PSCs, which helps in improving the performance of these solar devices. Cu:NiO x nanoparticles have been synthesized by a facile chemical method, and processed into a paste for screen printing. Extensive X-ray Absorption Spectroscopy (XAS) analysis elucidates the co-ordination of Cu in a NiO x matrix and indicates the presence of around 5.4% Cu in the sample. We fabricated a monolithic perovskite module on a 100 cm 2 glass substrate (active area of 70 cm 2 ) with a thin Cu:NiO x layer (80 nm), where the champion device shows an appreciated power conversion efficiency of 12.1% under an AM 1.5G illumination. To the best of our knowledge, this is the highest reported efficiency for such a large area perovskite solar device. I-V scans show that the introduction of Cu:NiO x mesoporous scaffold increases the photocurrent, and yields fill factor (FF) values exceeding 57% due to the better interface and increased hole extraction efficiency. Electrochemical Impedance Spectroscopy (EIS) results reinforce the above results by showing the reduction in recombination resistance (R rec ) of the PSCs that incorporates Cu:NiOx interlayer. The perovskite solar modules with a Cu:NiO x layer are stable for more than 4500 h in an ambient environment (25 °C and 65% RH), with PCE degradation of less than 5% of the initial value.