Studies on graft copolymerization of 4‐vinylpyridine onto guar gum

Graft copolymerization of 4‐vinylpyridine (4‐VP) onto guar gum (GOH) using potassium monopersulfate (PMS)/thioacetamide (TAA) as a redox pair was studied in an aqueous medium under inert atmosphere. The concentration of potassium monopersulfate and thioacetamide should be 1.0 × 10−2 and 5.0 × 10−3 mol dm−3, respectively, for highest grafting ratio and efficiency. Efficient grafting was observed at 19.25 × 10−2 and 4.87 × 10−2 mol dm−3 concentration of 4‐vinylpyridine and sulfuric acid, respectively. The optimum temperature for grafting is 30°C. As the time period of reaction is increased, the grafting ratio increases, whereas efficiency decreases. The plausible mechanism of grafting has been suggested. A sample of guar gum and guar‐ g‐4‐vinylpyridine were subjected to thermogravimetric analysis with the objective of studying the effect of grafting 4‐vinylpyridine on the thermal stability of guar gum.