High performance bio‐based thermosetting resins composed of tung oil and bismaleimide

The reaction of tung oil (TO) and 1,1′‐(methylenedi‐4,1‐phenylene)bismaleimide (BMI) in 1,3‐dimethyl‐2‐imidazolidinone (DMI) at 150°C for 4 h and subsequent precipitation gave TO/BMI prepolymer, which was cured at 200°C for 2 h gave crosslinked TO/BMI product with CC ratio from 1/1 to 1/4. The FE‐SEM analysis revealed that all the cured products are homogeneous and no phase separation was observed. The glass transition temperature and 5% weight loss temperature of the cured TO/BMI increased with increasing BMI content. The maximal tensile strength (38.1 MPa) and modulus (2.6 GPa) were obtained for the cured products with the CC ratios of 1/2 and 1/3, respectively. To evaluate the reaction of TO and BMI, the model reaction products of TO and N‐phenylmaleimide (PMI) in DMI were analyzed by 1H‐NMR spectroscopy. The NMR data of the reaction products of TO/PMI with the CC ratio 2/1, 1/1, 1/2, 1/3, and 1/4 at 150°C for 24 h revealed that Diels‐Alder reaction preferentially occurred at 2/1, and that ene reaction and other reactions such as radical homo and copolymerization gradually increased with decreasing CC ratio of TO/PMI.