Ultrathin cobalt silicide film formation on Si(100)

The interfacial reaction between ultrathin Co film and substrate Si(100) was studied by in situ XPS using monochromatized Al Kα. When the Co is deposited on Si(100) at room temperature, CoSi 2 is formed during the initial stage of Co deposition and then metallic Co starts to grow sequentially. For 8 ML Co deposition on Si(100) the interfacial reaction layer is relatively thin compared with the pure Co overlayer, which is not involved in the interfacial reaction in depth. The Co layers change rapidly to CoSi layers after annealing at 270°C, and then CoSi 2 layers form after annealing at 540°C for 2 min. The CoSi 2 layers are changed to CoSi 2 islands by post‐annealing at >650°C.