A new ball-on-disk vacuum tribometer with in situ measurement of the wear track by digital holographic microscopy

This contribution presents a new ball-on-disk vacuum tribometer with in situ measurement of the wear track by digital holographic microscopy. This new tribometer allows observation of the evolution of the wear track in situ and in real-time. The method combines a high vacuum high temperature ball-on-disk tribometer with a digital holographic microscope (DHM). The machine was tested and validated by taking DHM images during wear tests at room temperature and in vacuum at 2 · 10 −6 of polished 100Cr6 steel disks. We demonstrated that the DHM system is well suited to monitor the evolution of the wear track during sliding. We found that, with an acquisition time of 0.1 ms for the DHM, the maximal linear speed is 10 cm s −1 to have reliable images. We proved, via scanning electron microscope (SEM) pictures, that the lines in the sliding direction in all DHM images exist. We also validated the new tribometer by having an excellent correlation between the images and profiles of the wear track taken by the DHM with the ones from a confocal microscope. Finally, the new tribometer combined with the DHM has four advantages. It can test under vacuum and various atmospheric conditions. The evolution of the wear track is measured in situ and in real-time. Hence, the problem of replacing the sample is avoided. Thanks to the DHM technology, the vertical accuracy of the topographical measurement is 4 nm.