Minimizing microwave loss of amorphous hydrogenated silicon parallel-plate capacitors for superconducting integrated devices

Amorphous hydrogenated silicon (a-Si:H) based lumped elements are one of the promising ways for large-scale integration of superconducting quantum devices. We present a detailed study devoted to the plasma-enhanced chemical vapor deposition process parameters' influence on the structure and morphology of a-Si:H dielectric thin films. We experimentally demonstrate a microcrystalline-to-amorphous growth transition by changing the H2/SiH4 ratio and establish a relationship between the film's structure, thickness, and dielectric loss tangent (tan δ). It is shown that the best dielectric loss tangents of tan δLP = 4.5 × 10−5 (average 9.2 × 10−5) and tan δHP = 1.0 × 10−6 (average 1.2 × 10−6) for superconducting lumped elements with 350 nm-thick amorphous films can be achieved in single- and multi-photon regimes at sub-20 mK, correspondingly. These values are extracted by characterizing superconducting resonators with integrated parallel-plate capacitors (C = 0.2…6.0 pF) for a frequency range from 4.0 to 7.0 GHz. The presented low-loss a-Si:H films can be useful for various superconducting quantum applications, which is illustrated by the fabrication of lumped-element bandpass filters with a well-predicted amplitude–frequency response characteristic.