Influence of Chitosan–Sodium Tripolyphosphate-Coated Tung Oil Microcapsules on the UV Coating Performance of Cherry Wood Surface

By incorporating microcapsules with self-healing properties into the coating, a self-healing coating can be obtained, which can repair cracks or damage. In this study, chitosan–sodium tripolyphosphate-coated tung oil microcapsules 1# and 2# with a high encapsulation efficiency were incorporated into a UV-cured topcoat on cherry wood surfaces at different ratios. The results showed that as the microcapsule content increased, the coating’s reflectivity and gloss loss increased, while its impact resistance improved. However, the coating’s adhesion and hardness decreased. The coating containing 6% microcapsule 1# exhibited optimal performance on cherry wood board. The reflectance of the ultraviolet–visible light of the coating was 41.14%, the lightness value was 58.35, the red-green value was 13.96, the yellow-blue value was 25.32, the color difference was 4.47, the gloss reduction rate was 66.84%, the roughness was 1.11 μm, the impact resistance grade was level 4, the adhesion was level 1, the hardness was 3H, and the recovery rate was 17.06%. Comparative analysis revealed that both the chitosan/arabic gum-encapsulated tung oil microcapsules and chitosan–sodium tripolyphosphate-coated tung oil microcapsules could impart self-healing functionality to UV-cured coatings when incorporated into the finish. Notably, the coating system containing 6% chitosan/arabic gum-encapsulated tung oil microcapsules demonstrated optimal performance characteristics when applied to cherry wood substrates. The research findings demonstrate the technical feasibility of achieving self-healing functionality in UV-cured coatings for cherry wood surfaces.