Study on Dynamic Recrystallization Behavior and Numerical Simulation Prediction of Martensite Stainless Steel 04Cr13Ni5Mo

To address the coarse and mixed grain phenomena in ultra-large martensitic stainless steel forgings, this study investigated the hot deformation behavior of 04Cr13Ni5Mo martensitic stainless steel under deformation conditions of 950–1200 °C and strain rates of 0.001–0.1 s−1 using Gleeble-1500D thermomechanical simulation tests. Based on the experimental data, the flow stress curves of the steel were obtained, and a dynamic recrystallization (DRX) kinetic model was established. The model was then integrated into finite element software for simulation to verify its reliability, providing theoretical guidance for optimizing high-temperature forging processes. The results demonstrate that dynamic recrystallization in 04Cr13Ni5Mo steel occurs more readily at temperatures above 1050 °C and strain rates below 0.1 s−1. Under the selected hot compression test condition (1100 °C/0.01 s−1), the simulated grain size in the central deformation zone was 48.98 μm, closely matching the experimentally measured value of 48.18 μm. This agreement confirms the reliability of finite element-based prediction and control of grain size in martensitic stainless steel forgings.