The Effect of Interrupted Loading on the Lüder Phenomena in AISI 1524 Steel Alloy

Under specific temperature and strain rate conditions, certain materials, such as low-carbon steels and select magnesium and aluminum alloys, experience a localized deformation phenomenon known as the Lüders effect. This behavior manifests as a well-defined yield point, after which the stress–strain response transitions into a plateau phase. Experimentally observed through full-field tests, the Lüders effect appears in the form of a band(s). This manuscript presents, for the first time, a systematic study of interrupted loading on the Lüders phenomenon in AISI 1524 hot-rolled steel, using uniaxial tensile testing combined with digital image correlation (DIC). While similar approaches have been applied to other alloys, no prior work has reported on AISI 1524 steel under unloading–reloading cycles during the Lüders plateau. Interruptions in loading involved unloading at 25%, 50%, and 75% of the total plateau region independently until stress approached zero, followed by reloading at the same rate until failure. Each unloading case was subjected to two tests, alongside two additional control tests where loading proceeded without interruption. Based on the findings of this study, it can be inferred that the Lüders phenomenon in AISI 1524 steel exhibits a decrease in strain intensity upon unloading, along with an extension of the Lüders plateau when interrupted loading occurs up to halfway through the plateau region. However, implementing an interrupted loading regime at three-quarters of the plateau had minimal to no discernible effect on the phenomenon. The majority of samples displayed two Lüders bands, a few exhibited either a single band or three bands, suggesting a complex relationship with material heterogeneity and specific impurities present in each sample. The novelty of this work lies in showing how controlled unloading–reloading cycles alter both the propagation and characteristics of Lüders bands in AISI 1524 steel.