Scratch Resistance and Tribological Enhancement of Epoxy Composites Reinforced with Chopped Glass Fiber and Nano Silica Through Taguchi Analysis

This study examines the incorporation of chopped glass fiber and nano-silica into epoxy, focusing on their effects on the tribological and mechanical properties. Three reinforcement ratios (1 wt.%, 3 wt.%, and 5 wt.%) were analyzed by scratch tests and profilometric analysis. The coefficient of friction (COF), scratch depth, and scratch width values of the unreinforced epoxy resin were measured as 0.45, 37.73 µm and 479 µm, respectively. The addition of glass fibers contributed to improved scratch performance by restricting material removal and stabilizing groove morphology, although higher fiber ratios caused an increase in COF. The results indicated that nano-silica increased scratch resistance with a COF of 0.42 at 5 wt.%, giving a scratch depth of 19.92 µm and a scratch width of 166 µm. Glass fiber also improved scratch performance, although there were high COF values for higher ratios, which could be due to the aggregation effect of the fibers. Statistical validation of the results was carried out through the Taguchi method and ANOVA analyses. These analyses showed that reinforcement type and ratio played an important role in scratch behavior. SEM analyses of worn surfaces showed that nano-silica can dissipate stress and minimize plastic deformation to yield improved scratch morphology. Overall, the results emphasize the complementary role of glass fiber and nano-silica reinforcements in improving the scratch resistance of epoxy resin for industrial applications.