Investigation of the Possibility of Utilizing Man-Made Waste to Produce Composite Binders

In this article, composite binders based on industrial waste—phosphogypsum, granular phosphoric slag, and burnt barium carbonate tailings––are investigated. It was found that the optimal composition (65% slag, 20% phosphogypsum, 15% tailings) provides compressive strength up to 31.1 MPa after steaming, which corresponds to grade M300 cement. Replacing natural gypsum with phosphogypsum increases strength by 5–10%, and using waste reduces cost by 20–25% compared to traditional binders. This technology eliminates the need for high-temperature firing, reducing energy consumption by 40–50%. Neutralization of harmful impurities of phosphogypsum with oxides of MgO and CaO reduces the ecotoxicity of the material by 70–80%. It is shown that hydrothermal treatment accelerates hardening, providing 90% of brand strength in 28 days. The developed binders are promising for the production of building blocks, road surfaces, and land reclamation.